Stainless Steel Welding Wire
Stainless Steel Welding Wire
Standard: AWS A5.9/A5.9M:2006 An American National Standard.
YIETO manufactured in grades 307, 308, 308L, 308LSi, 308LMo, 309, 309L, 309LSi, 309LMo, 310, 312, 316, 316L, 316LSi, 317L, 318, 320, 321, 347, 347Si, 383, 385, 409, 409Nb, 410, 410NiMo, 420, 430, 439, 446LMo, 630, 630, 2209, 2553, 2594, 3556.
★ GMAW (MIG) - GAS METAL ARC WELDING WIRE
MIG wire bright drawn/ bright finish / soap drawn (de-coated) matte finish in precision layer wound spools .
Sizes (mm): 0.8, 1.0, 1.2, 1.6, 2.0.
★ GTAW (TIG) - GAS TUNGSTEN INERT ARC WELDING WIRE
Tig Wire Bright Drawn Bright Finish in cut length 1000 mm, Grade is embossed on the head of wire.
Sizes (mm): 1.6, 2.0, 2.4, 3.2, 4.0.
★ SAW - SUBMERGED ARC WELDING WIRE
SAW wire bright drawn/ bright finish / soap drawn (de-coated) matte finish in precision layer wound spool
Sizes (mm): 1.2, 1.6, 2.0, 2.4, 3.2, 4.0.
★ CORE WIRE FOR WELDING ELECTRODE
Core wire is produce welding electrode, hot rolled & annealing & pickling finish.
Sizes (mm): 1.6 , 2.0, 2.4, 3.2, 4.0, 5.0.
Product Description
CLASSIFICATION : AWS/SFA-5.9: ER316L, EN 12072 19 12 3 L
DIN 8556: WK. 1.4430
CHARACTERISTICS : ER316L is austenitic Stainless steel low carbon welding wire of 18 Cr%, 12 Ni% and 2 Mo%. The weld metal contains ferrite and resistance to crack is extremely good. Low carbon assists austenitic arc stability and improves corrosion resistance such as intergranuler type. The mechanical properties of the weld metal are good.
APPLICATION : ER 316L molybdenum type grade for the MIG,TIG and SA welding of similar type stainless steels. The molybdenum vastly improves the resistance of pitting corrosion, particularly in chloride solutions and the low carbon grades further improves resistance to intergranular corrosion. Suitable for welding SS 316L, SS 318 grades. The weld metal is recommended for high temperature service up to 350°C
SHIELDING GAS : welding with 100% Ar gas Or Ar+2%O2 gas.
| C | Mn | Si | S | P | Ni |
| 0.030 max. | 1.00-2.50 | 0.30-0.65 | 0.030 Max | 0.030 Max | 12.00-14.00 |
| Cr | Mo | Cu | |||
| 18.00-20.00 | 2.00-3.00 | 0.75 Max |
| UTS (N/mm²) |
Proof strength (N/mm²) |
EL % (5d) | CHARPY “V” NOTCH IMPACT AT |
FERRITE Qty.(FN) |
| 550-680 | 390-480 | 30-40 | +20°C : 80-120 J -196°C : 50-70 J |
7-9 |
| Size(mm) | Size(inch) | Current Condition (DC+) | Voltage (V) | Gas Flow Rate L/min. | Spool packing 12.5 kg. | Spool packing 15 kg | Drum packing 100/200kg |
| 0.80 | 0.031 | 60-180 | 16-24 | 10-20 |  |
|
X |
| 1.20 | 0.047 | 120-300 | 24-34 | 15-25 | |
|
|
| 1.60 | 1/16” | 150-350 | 28-36 | 15-30 | |
|
|
| Size(mm) | Size(inch) | Length(mm) | Length (inch) | Current Condition(DC+) | Voltage(V) | Tube packing 5 kg | Box packing 20 kg |
| 1.60 | 1/ 16” | 1000 | 36” | 40-80 | 10-16 | |
|
| 2.0 | 5/ 64” | 1000 | 36” | 50-100 | 12-18 | |
|
| 2.4/ 2.5 | 3/ 32” | 1000 | 36” | 60-120 | 14-20 | |
|
| 3.2 | 1/ 8” | 1000 | 36” | 100-150 | 16-24 | |
|
| 4.0 | 5/ 32 | 1000 | 36” | 140-200 | 18-28 | |
|
And also available RAAJMIGER308LSi version for MIG welding process